Automated fiber placement

Automated fiber placement (AFP), also known as advanced fiber placement, is an advanced method of manufacturing composite materials. These materials, which offer lighter weight with equivalent or greater strength than metals,[1] are increasingly used in airframes and other industrial products.

Fiber Placement is an automated composites manufacturing process of heating and compacting synthetic resin pre-impregnated non-metallic fibers on typically complex tooling mandrels. The fiber usually comes in the form of what are referred to as "tows". A tow is typically a bundle of carbon fibers impregnated with epoxy resin and is approximately 0.500 inches (12.7 mm) wide by 0.005 inches (0.13 mm) thick and comes on a spool. Fiber placement machines (FPM) generally have a capacity of 12 to 32 tows or when placing all tows at a time in a course, have respective course widths of 1.5 in to 4 in. The tows are fed to a heater and compaction roller on the FPM head and through robotic type machine movements, are placed in courses across a tool surface. Courses are generally placed in orientations of 0°, +45°, -45° and 90° to build up plies which in combination, have good properties in all directions. Fiber placement machines are generally rated in (lb/h), (lb/min) or weight per time.

Description

Automated fiber placement (AFP) machines are a recent development of composite manufacturing technologies meant to increase rate and precision in the production of advanced composite parts.[2] AFP machines place fiber reinforcements on moulds or mandrels in an automatic fashion and use a number of separate small width tows (typically 8 millimetres (0.31 in) or less) of thermoset or thermoplastic pre-impregnated materials to form composite layups. This technology allows better precision and increased deposition rates when compared with experienced laminators but, while allowing for more complex layup geometries than Automated Tape Laying (ATL) it does not reach the same deposition rates. Automated fiber placement can be used to manufacture complex structures that are not possible to manufacture with any other methods.[3]

See also

References
  1. "What is Automated Fibre Placement". Composites Evolution. January 19, 2021.
  2. Lukaszewicz, Dirk; et al. (2012). "The engineering aspects of automated prepreg layup: History, present and future". Composites Part B: Engineering. 43 (3).
  3. Ridgard, C. (2009). "Out of autoclave composite technology for aerospace, defense and space structures". International SAMPE Symposium and Exhibition. 54.
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.